BLDE+ZN electrogalvanized plates and strips are featured with good erosion-resistant, high surface quality(O5 plate surface are available) and excellent processing and coating performances. They can be used to manufacture inside an outside automotive plates , structural parts and reinforcements.
BLDE+ZN electrogalvanized automotive plates sizes:
Nominal thickness: 0.30mm~2.0mm, nominal width: 800mm~1830mm
(Note: nominal thickness of a plate/strip is sum of base plate thickness and coating thickness.)
BLDE+ZN electrogalvanized automotive plates mechanical and process performances:
The mechanical and process performances of pure zinc coated plates/strips must comply with the stipulations of those of relevant base plates. The base plate grade is BLC, and the corresponding base plate standards is Q/BQB 408-2003.
Among the mechanical performances of Zn-Ni alloy coated plates/strips, breakage percent elongation is allowed to be lowered by 2 units against that of relevant base plates, r is allowed to be lowered by 0.2 against that of relevant base plates and other mechanical and process performances shall comply with the stipulations of those of relevant base plates.
BLDE+ZN cold rolled coils available coating weight range is given in the following table:
g/㎡
Coating Form |
Coating variety |
|
Pure zinc coating (single-side) |
|
|
Equally coating |
3~90 |
|
Differential coating |
3~90, max. coating thickness difference between two sides: 40 |
|
Single-side coating |
10~110 |
|
Note: 50g/㎡ pure zinc coating weight is equivalent to about 7.1μm |
|