A542 have Five grades or levels. They are : grade A, grade B, grade C, grade D, grade E . A542 Grade E need to be done the (Quenching + Tempering ) heat-treatment to meet the property requirement in the standard ASTM A-542/A-542M.
ASTM A542 Grade E in the standard A-542/A-542M is a kind of Mo-V alloy steel plates material used to fabric high temperature pressure vessels.
Standard : ASTM A-542/A-542M
Dimension range :3mm -260mm x 1000mm-4000mm x 1000mm-18000mm
ASTM A542 Grade E steel plate/sheet Mechanical Properties :
|
Mechanical Properties
|
||||||
|
Grade |
Thickness |
Yield |
Tensile Strength |
Elongation |
Charpy V Notch Impact Test |
|
|
Degree |
Min Value |
|||||
|
A542 Grade E |
mm |
Min Mpa |
Mpa |
Min % |
- |
J |
|
5≤t≤50 |
55（380） |
85-110（585-760） |
20 |
- |
||
|
Note: Impact energy for impact test is on longitudinal |
||||||
A542 Grade E Boiler steel plate Chemical Composition :
|
Chemical Composition
|
|||||||
|
Grade |
The Element Max (%) |
||||||
|
C |
Si |
Mn |
P |
S |
Cr |
Mo |
|
|
A542 Grade E |
≤0.18 |
0.15 |
0.25-0.66 |
0.010 |
0.010 |
2.63-3.37 |
0.85-1.15 |
|
Ni |
V |
|
|
|
|
|
|
|
≤0.28 |
≤0.18 |
|
|
|
|
|
|
① In A 542/A 542M-82 standard and the earlier standard, the steel plates whose thickness ≤ 125mm, C must be ≤ 0.15%
② Ca can be replace by REM as the agreement with manufacturer and buyer, if like this, then the total amount of REM should be stated.
Delivery Status : Quenching + tempering
ASTM A542 Grade E Ni alloy steel plate/sheet application :
A542 Grade E steel plate is mainly used in petroleum, chemical industry, power station, boiler and other industries, for the production reactor, heat exchanger, separator, spherical tank, oil tank, liquefied gas tank, nuclear reactor pressure shell, boiler drum, liquefaction Oil cylinders, high-pressure water pipe hydropower station, turbine volute and other equipment and components.